Aluminum environmental automated brazing filler metals solder wire alloy

R&D background
In recent years, as copper becoming a scarce strategic resource,the price of electrolysis copper increased so high that theconsumers  in the entire materials industry are choosingaluminum instead of copper; which is carried forward and processedsmoothly and quickly through materials scientist and a group ofenterprises. And in some specific field, aluminum replaces copperhas implemented successfully. While, there also exist problem inaluminum brazing industry.

Three advantages of JH-001L environmental automatic brazingaluminum solder
1. automatic brazing  solder, without smearing corrosive weldpaste and flux during welding. 2. Brazing directly, cut offsmearing brazing flux process and improved product efficiency.3.Without cleaning after welding for non-corrosion materials onsurface.

Applications: Aircraft engine unit, Heat exchangers,Refrigeration air conditioner aluminum evaporator, Condenser,Freezer, Aluminum alloy tube.

Model: JH-001L-K,JH-001L-Q,JH-001L-P     Environmental automatic brazing aluminum solder
Ingredient: AL Si Se Rera earth
Solidus: 560,565,570
Liquidus: 580,580,585
Specification:  1.6-3.0    2KG/Roll ,5KG/Roll
Shape: Strip,Ring,Roll,Paste
Application: JH-001L-K: Refrigeration air condition aluminumevaporator
 JH-001L-Q:Automobile air conditioner condenser, evaporator,radiator, pipe pieces
 JH-001L-P:Aluminum evaporator, condenser, and tube unity forlarge-scale cold storage
Brazing Method: Manual flame brazing, automatic flame brazing, high frequency brazing and soldering in the furnace
Anti-corrsion Test Qualified at more than 500hrs salt spraytest
Joint Strength 1.8 times of parent materials strength
Sample: Free